拉丝冷却循环水系统防腐阻垢探讨

第31卷第3期金属制品2005年6月Vol. 31No. 3Steel Wire ProductsJune2005拉丝冷却循环水系统防腐阻垢探讨静恩志杨义纲(宁夏恒力钢丝绳股份有限公司 石嘴山753202 )关键词拉丝 泠却循环水防腐中图分类号TC174拉丝冷却循环水系统在运行过程中,存在结表1各指标的控制要求垢、喷嘴及窄缝处易堵塞现象。水垢、锈垢、油垢的指标循环水控制值分析频率.导热系数一般不超过1.16 W/( m' K)钢材的导热pF9~121次/日系数为45 W/( m. K )。结垢后换热效率大大降低钢丝在卷筒上得不到充分冷却,积累温度超过盐度TSD TSD福环水/ TSD自来水=5~ 10夏季2次/周冬季1次/周160C易产生时效脆化现象,钢丝强度偏高,扭转值偏低结垢引起设备腐蚀,使用寿命缩短。浓缩倍率Ca-循环水/Ca-自来水=5 ~夏季 2次/周1(表2 pH 值和TSD值选择1方案选择取循环TSD/加入量/防腐阻垢主要采用机械和化学药剂两种方法。H水样/L，( mg" L小) (g:门)卷筒内壁形成垢层1mm以上后很难清除。试过多0.510. 81101 000种方法均不理想。1.010.08500选择.上海昱真水处理公司的方案根据循环水的水质情况和垢样分析配制除垢药剂YZ101在不1.59.778333停产情况下使用阻垢剂3个月观察效果。1. 89.670278操作注意事项( 1 )当pH值和TSD值超标后应2防腐阻垢剂的使用适当排污补水补水后应按规定量补投药剂(2)因2.1 阻垢原理为药剂对皮肤有一定 的腐蚀性,最好将药剂溶解后YZ101防腐阻垢剂是黑色固状混合物当pH≥再投入池中(3 )若投药量不足时pH值偏低,-定9时能有效地稳定水中各种结垢物质。可与NaOH保证pH值≥9不能光靠加碱调整pH值,否则不能配合使用提高水的pH值。阻垢原理( 1 )在运行很好地发挥药剂阻垢除垢功能。中除掉水系统的垢和锈,相当于除掉了腐蚀电池的阴极使得以电化学腐蚀为主的水系统只剩下金属3试用结果阳极,从根本上阻止了腐蚀(2)在金属表面形成-使用2个月后钢丝力学性能试验结果见表3。薄层黑亮的保护膜,从而抵抗腐蚀( 3 )pH≥10 ,使表3使用 YZ101前后钢丝力学性能试验数据铁处于钝化区。生产直径/设备总验合格一次合2.2 使用方法日期mm量/盘量/盘格率/%使用防腐阻垢剂的控制要求见表1。3.11 5.5- >2.2 LZ10/550* 66 5"86. 36取YZ 101溶液0.5g pH值和TSD值见表2。中国煤化工。7 3982. 98每吨水按300g阻垢剂加入量(根据不同设备fTHCNMHG138129 93. 48LL1W/JJJ和使用条件对药剂配方、投药量进行适当调整)采5.115.5- +2.28 LZ10/5503 50 44 88. 00用pH计和TSD计每日测循环水pH值一次,一般5.135.5-→2.4 LZ10/5503 83 7893. 98.维持9~12每周测一次TSD其循环倍率≤10。5.96.5→3.0 LZ8/700'264148 93. 94第31卷第3期金属制品2005年6月Vol. 31No. 3Steel Wire ProductsJune2005英国线材制品工业研究窦光聚(郑州金属制品研究院450007)滴要研究英国线材制品在钢铁工业中的地位线材及其- - 次制品、二次制品的生产、消费、进出口现状及发展规律。研究表明英国线材消费较低,只有钢铁总消费的7%线材消费量只有线材产量的70%线材出口比例较大,占产量的50%以上线材加工比例较高并呈上升趋势2003年线材深加工比例达到77%钢丝制品的表观消费大于生产量2003年产量比表观消费低11. 5%。关键词英国线材钢丝制品生产消费进出口.中图分类号T- 103.Wire Rod Products Industry Investigation of UKDou Guangju( Zhengzhou Steel Wire Products Research Institute 450007 )Abstract To investigate the wire rod products status of UK in iron and steel industry , the present situation and develop-ment laws of production , consumption , import and export of wire rod and its primary products and further products. The in-vestigation indicates that the wire rod consumption in UK is lower , which has only 7% of total consumption of iron andsteel , the consumption of wire rod occupied only 70% of shipment of wire rod ; the export proportion of wire rod is higher ,which occupied over 50% of output ; the proportion of wire rod processing is higher and takes on rising trend , which gets upto 77% in 2003 ;the apparent consumption of wire products is more than apparent output , the apparent output is lower 11.5% than consumption in 2003.Keywords UK ; wire rod ;steel wire products ; production ; consumption ; import and export英国是一个发达的工业化国家人口约60001线材在钢铁工业中的地位万2003 年GDP达到10 346亿英镑。英国的钢英国1994- -2003 年年人均钢铁消费在240 ~铁国内生产量为1 326.6万t ,在世界排名第17280 kg。2003 年英国的钢铁消费为1290万t ,不同位2。本文研究英国的线材制品工业现状及发展类型的钢材消费比例如图1所示。其中板卷带(含规律。薄板、宽厚板、热轧卷、冷轧带钢)占45%型材占检查LZ8/700拉丝机第12号车的拉丝卷筒使用除垢剂后每天节水80t ,每月节省因清理内壁,上面的锈垢用钢刷全部能刷掉,管道畅通无卷筒水路的停机时间16h。以4台拉丝机生产500 t阻;使用3个月后, 检查LZ8/700拉丝机1号车第7成品钢丝推算,-年可降低10万元成本。号卷筒,内壁不再长新的锈垢并有- -层不太均匀的(收稿日期2004-12-23 )黑膜(保护膜);查看LZ10/550拉丝机3号车第1中国煤化工号卷筒筒内壁锈垢已自动除净表面光滑。试验表静恩YHCNMHG&绳股份有限公司技术研明经过3个月的使用拉丝机冷却循环水系统的结发部工程师。垢已经被除掉提高了钢丝的一次试验合格率。杨义钢1938年生宁夏恒力钢丝绳股份有限公司教授级高级工程师，已退休。.4结语