ASTM C1863-2018 用直接加压法在环境温度下测定连续纤维增强先进陶瓷复合材料管试样环向拉伸强度的方法 Standard Test Method for Hoop Tensile Strength of Continuous Fiber-Reinforced Advanced Ceramic Composite Tubular Test Specimens at Ambient Temperature Using Direct Pressurization

1.1 This test method covers the determination of the hoop tensile strength, including stress-strain response, of continuous fiber-reinforced advanced ceramic tubes subjected to direct internal pressurization that is applied monotonically at ambient temperature. This type of test configuration is sometimes referred to as “tube burst test.” This test method is specific to tube geometries, because flaw populations, fiber architecture, material fabrication, and test specimen geometry factors are often distinctly different in composite tubes, as compared to flat plates. 1.2 In the test method, a composite tube/cylinder with a defined gage section and a known wall thickness is loaded via internal pressurization from a pressurized fluid applied either directly to the material or through a secondary bladder inserted into the tube. The monotonically applied uniform radial pressure on the inside of the tube results in hoop stress-strain response of the composite tube that is recorded until failure of the tube. The hoop tensile strength and the hoop fracture strength are determined from the resulting maximum pressure and the pressure at fracture, respectively. The hoop tensile strains, the hoop proportional limit stress, and the modulus of elasticity in the hoop direction are determined from the stress-strain data. Note that hoop tensile strength as used in this test method refers to the tensile strength in the hoop direction from the introduction of a monotonically applied internal pressure where ‘monotonic’ refers to a continuous nonstop test rate without reversals from test initiation to final fracture. 1.3 This test method applies primarily to advanced ceramic matrix composite tubes with continuous fiber reinforcement: unidirectional (1D, filament wound and tape lay-up), bidirectional (2D, fabric/tape lay-up and weave), and tridirectional (3D, braid and weave). These types of ceramic matrix composites can be composed of a